Our Company Sturdy Industries Ltd. has installed state- of-the-art( properzi) continuous casting and rolling mill at Baddi,( H.P.) with capacity to produce 15,000 MT wire rods annually of 9.5 mm dia (EC grade/alloy rods) to cater to the needs of conductor (AAAC, AAC, and ACSR) and cable industry.


We manufacture aluminum wire rod EC Grade 1370 9.5mm , 12mm diameters.

Packing are Export standard packing (In coil, coil weight range 2.0tons – 2.50 tons)ALUMINUM RODS
Size: Φ9.5mm、Φ12mmChemical elements:
Al99.7%min, Fe 0.05~0.18%,Si 0.03~0.09%, Cu 0.005%Physics Specification:
Conductivity: 61.55%IACS min; Tensile st.
95~110Mpa;110~120Mpa;110~130Mpa; Elongation 8~15;Electric Resistivity
At 20 Degrees C µΩcm Max 2.081.Packing:
Export Packing We are exporting to Korea, Japan, Canada,
USA, France, Singapore, Europe, Africa etc more than ten countries and areas,
we have obtained the certificate of ISO9001-2000.delivery is very fast .
PLANT & MACHINERY
For Continuous Casting & Rolling of EC Grade Aluminium/Aluminium Alloy Rods. Melting & Holding furnaces and Casting & Rolling Mill. Degassing System fitted with induction heating system for on line solution treatment to manufacture Aluminum Alloy Rods. Ageing Furnaces for Aluminum Alloy Conductors
SPECIFICATIONS OF WIRE RODS
Conductivity: 61.55% IACS min;Tensile st.95~110Mpa,110~120Mpa,120~130Mpa;
Elongation: 8~15;Electric Resistivity At 20 Degrees C; µOcm Max 2.081.
Chemical Composition Spectral Results: Al. 99.71%, Fe 0.23, Si 0.045,
Cu 0.002, Zn 0.006, Mn 0.001, Mg 0.001, Cr 0.001, B 0.005
APPLICATIONS
Electrical Conductor (EC) wire rods are used for the production of cables and ACSR and AAC conductors.
Alloy wire rods are used to produce AAAC .

QUALITY CONTROL

  • Our Wire Rod quality exceeds ASTM, DIN, BS, JS and other internationally accepted quality standards.
  • The company has fully equipped testing laboratory and engineers to test mechanical and electrical properties of wire rods and deliver world class product.
  • Testing equipment include spectrometers, tensile testing machines, along with complete range of necessary equipments .We have set up modern & latest spectrometer for of elemental analysis of EC & Alloy Wire Rods. Raw material to finished products are tested on spectrometer so that high quality products is delivered to customer without any impurities.
  • Certificate of breaking load, elongation, conductivity and elemental analysis report is supplied with each lot. We process only high quality aluminium ingots procured from primary producers with purity more than 99.70% to manufacture aluminium EC & aluminium Alloy wire rods.

We supply 1350 EC aluminium wire rod , aluminium alloy wire rod 6201 .

Quick dispatches guaranteed .

The specifications are given below-

SPECIFICATION SHEET FOR AWR T-4

1 APPLICABLE STANDARD IS-9997-1981
2 METHOD OF PRODUCTION CONTINUOUS CASTING AND ROLLING
3 TEMPER T-4
4 DIAMETER OF ROD 9.5+/- 0.5 MM
5 TENSILE STRENGTH 160 M Pa or 16.3 kg/mm2
6 ELONGATION (ON 250 MM GAUGE LENGTH) -Min 12%
7 ELECTRICAL RESISTIVITY-MAX 3.44 Microhm-Cm at 20 deg C
8 ELECTRICAL CONDUCTIVITY 50% IACS min.
9 CHEMICAL COMPOSITION
SILICON 0.50-0.90 %
MAGNESIUM 0.60-0.90 %
IRON 0.50 % MAX
COPPER 0.10 % MAX
ZINC 0.10 % MAX
MANGANESE 0.03 % MAX
CHROMIUM 0.03 % MAX
BORON 0.06 % MAX
OTHER ELEMENTS 0.03 % EACH SUBJECT TO TOTAL OF 0.10%

A1350 Rod Specifications

S.No Parameter Unit Specification
1 UTS Mpa 83-90
2 Conductivity %IACS min. 61.5
3 Elongation % Min. 20
4 Diameter mm 9.5 ± 0.5
5 Coil Weight MT 2.0 ± 0.1
6 ID mm 570
7 OD mm 1350 – 1400
8 Height mm 850 – 870
Mode of Packing – Eye to Sky

Type 1:

Aluminium rod for production of conductors for electrical purpose

According to ASTMB-233

Nominal Diameter:

9,5 mm +/- 5% of nominal diamater; 3% tolerance on out-of-roundness

Mechanical and electrical characteristics

Temper               kg/mm2              elongation %     resistivity            Conductivity IACS min %
H11                        8,15 – 9,68          25                           2,785                     61,9
H12                        9,68 – 11,21        20                           2,801                     61,5
H13                        10,71 – 12,23     16                           2,801                     61,5
H14                        11,72-13,25        14                           2,801                     61,5

Application

H11: enamelled, insulated, cable conductors – bare

H12: insulated, cable conductors – bare

H13/H14: overhead conductors

Chemical composition:

Si            0,15% max

Fe           0.30% max

Cu          0,02% max

Zn           0,05% max

Ti            0,02% max

Mn         0,03% max

Mg         0,03% max

other    0,03% all

Al:          99,5% min


Conditions of supply:

Wound into continuous-length coils without junction, preferable vertical axe, weight 2000 kg +/- 10%

Coils:

Inner diam: 530 mm min – 770 mm max

Outer diam: 1440 mm max

Width : 900 mm max

Marking:

Manufacturer name or trade mark

Rod designation and temper

Cast number and coil number

Nominal diameter

Net weight in kg

Accompanied with test certificate and packing list

Type 2:

Aluminium Alloy wire rod 6101 – ASTMB 317 – temper T6

Wire Rods – UTS & Conductivity

EC Grade

Temper  UTS (MPa) Conductivity (%)
O 59 – 97 61.8
H12 83 – 117 61.5
H14 103 – 138 61.4
H16 117 – 152 61.3

Alloy Grade

Temper  UTS (MPa) Conductivity (%)
O 90 – 159 55.0
M 147 – 227 53.0